Alloy Plastic )Soluble HIPS milk white opaque wire support materials. The density is 1.05 g/cm ^ 3. Melt temperature of 150 ~ 180 ℃. Print temperature 230 ℃ to 265 ℃, the thermal decomposition temperature of 300 ℃. Dissolved in limonene, at room temperature due to the low gloss surface is inferior smooth materials, printing surface effect is more exquisite appearance alone but comprehensive performance impact strength is low.Cooperate with ABS print as support material easy to dismantle.
PVA water-soluble support materials, soluble in water at room temperature environment, without adding any solvents, support, environmental non-toxic harmless to the human body is a kind of environmental protection material.
As the different brands of 3D printer design of the print head temperature there will be temperature difference can refer to the table using the temperature: ABS printing temperature can be between 230 degrees -260 degrees, PLA use temperature between 190 degrees -230 degrees. Remote wire feeding frame printing temperature than the direct feeding print fabric to 5 ℃ -15 ℃, different 3D printer in the print before you test the effect of silk, and then make the appropriate adjustment temperature, find the right to print their own temperature and then print So that supplies and machines with each other to achieve better print results.
Please refer to the product data sheet for specific printing temperature.
Physical properties of materials | Testing standards | ABS | Flame retardant ABS | HIPS | FLEX | MAX | WOOD | Bamboo | PLA | WOOD | Bamboo | PLA |
Specific Gravity | D792 | 1.05 | 1.17 | 1.05 | 1.2 | 1.27 | 1.05~1.18 | 1.0~1.18 | 1.24 | 1.05~1.18 | 1.0~1.18 | 1.24 |
Heat change temperature H.D.T Annealed(85℃,8hr) Unannedaled |
1/4",120℃、hr |
99(210) 88(190) |
85(185) 76(169) |
90 | / | 70(0.455Mpa(66psi) | 65 | 65 | 60 | 65 | 65 | 60 |
MFR(200°C,g/10min) | 200℃,5kg | 1.8 | 4.8 | 8 | 12.1 | 20(250℃2.16KG) | 8~18 | 8~18 | 5~12 | 8~18 | 8~18 | 5~12 |
Bending strength (MPa)Tensile Strength@Break,psi | ASTM D790 | 820(11660) | 640(kg/c㎡) | D638/450 | / | Mpa(kgf/cm2)71(720) | 5500 | 5500 | 7770 | 5500 | 5500 | 7770 |
Tensile Elongation,% | ASTM D638 | 20 | 15 | 40 | >400 | 4.5 | 5.5 | 5 | 6 | 5.5 | 5 | 6 |
Notched lzod lmpact,ft-lb/in(J/m) | ASTM D256 |
18(3.3) 20(3.7) |
3.8 | 11 | 85 | 85 | 0.06 | 0.06 | 0.1(16) | 0.06 | 0.06 | 0.1(16) |
Printing temperature | ℃ | 220℃-260℃ | 220℃-260℃ | 210℃-260℃ | 195℃-245℃ | 230℃-260℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ |
Mr Yang
Mobile site