XYD-METAL consumable mainly in metal powder as auxiliary substrate and compatible combination, through a special production process of mixed production it becomes linear consumable for the use of FDM printing. The print can be sanded to remove surface mixture shows the metal powder by grinding effect. The texture and the proportion could make you experience FDM metal printing feelings.
Printing temperature
Product Features
Product specifications
Packing| Physical properties of materials | Testing standards | ABS | Flame retardant ABS | HIPS | FLEX | MAX | WOOD | Bamboo | PLA | WOOD | Bamboo | PLA |
| Specific Gravity | D792 | 1.05 | 1.17 | 1.05 | 1.2 | 1.27 | 1.05~1.18 | 1.0~1.18 | 1.24 | 1.05~1.18 | 1.0~1.18 | 1.24 |
|
Heat change temperature H.D.T Annealed(85℃,8hr) Unannedaled |
1/4",120℃、hr |
99(210) 88(190) |
85（185） 76（169） |
90 | / | 70(0.455Mpa(66psi) | 65 | 65 | 60 | 65 | 65 | 60 |
| MFR(200°C，g/10min) | 200℃,5kg | 1.8 | 4.8 | 8 | 12.1 | 20(250℃2.16KG) | 8~18 | 8~18 | 5~12 | 8~18 | 8~18 | 5~12 |
| Bending strength (MPa)Tensile Strength@Break,psi | ASTM D790 | 820(11660) | 640（kg/c㎡) | D638/450 | / | Mpa(kgf/cm2)71(720) | 5500 | 5500 | 7770 | 5500 | 5500 | 7770 |
| Tensile Elongation,％ | ASTM D638 | 20 | 15 | 40 | ＞400 | 4.5 | 5.5 | 5 | 6 | 5.5 | 5 | 6 |
| Notched lzod lmpact,ft-lb/in(J/m) | ASTM D256 |
18(3.3) 20(3.7) |
3.8 | 11 | 85 | 85 | 0.06 | 0.06 | 0.1（16） | 0.06 | 0.06 | 0.1（16） |
| Printing temperature | ℃ | 220℃-260℃ | 220℃-260℃ | 210℃-260℃ | 195℃-245℃ | 230℃-260℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ |